SPECIFICATION
Supplier : Samsung electro-mechanics
Product : Multi-layer Ceramic Capacitor
A. Samsung Part Number
CL
①
①
Series
②
Size
③
Dielectric
④
Capacitance
⑤
Capacitance
tolerance
⑥
Rated Voltage
⑦
Thickness
10 V
0.5 ± 0.05 mm
05
②
B
③
104
④
K
⑤
P
⑥
5
⑦
N
⑧
N
⑨
W
⑩
C
⑪
Samsung P/N :
CL05B104KP5NNWC
Description :
CAP, 100㎋, 10V, ±10%, X7R, 0402
Samsung Multi-layer Ceramic Capacitor
0402 (inch code)
X7R
100
㎋
±10 %
L: 1.0 ± 0.05
mm
W:
Ni
Cu
Sn 100%
Normal
Product for Network application
Cardboard Type, 7" reel
(Pb Free)
0.5 ± 0.05 mm
⑧
Inner electrode
Termination
Plating
⑨
Product
⑩
Special
⑪
Packaging
B. Samsung Reliability Test and Judgement condition
Performance
Capacitance
Tan
δ
(DF)
Insulation
Resistance
Appearance
Withstanding
Voltage
Temperature
Characterisitcs
Adhesive Strength
of Termination
Bending Strength
Solderability
Within specified tolerance
0.05 max.
10,000Mohm or 100Mohm㎌
Whichever is Smaller
No abnormal exterior appearance
No dielectric breakdown or
mechanical breakdown
X7R
(From -55℃ to 125℃, Capacitance change shoud be within ±15%)
No peeling shall be occur on the
500gF, for 10±1 sec.
terminal electrode
Capacitance change :
within ±12.5%
Bending to the limit (1mm)
with 1.0mm/sec.
More than 75% of terminal surface
is to be soldered newly
SnAg3.0Cu0.5 solder
245±5℃, 3±0.3sec.
(preheating : 80~120℃ for 10~30sec.)
Resistance to
Soldering heat
Capacitance change :
Tan
δ,
IR : initial spec.
within ±7.5%
Solder pot : 270±5℃, 10±1sec.
Rated Voltage
60~120 sec.
1㎑±10%
Test condition
1.0±0.2Vrms
Microscope (10)
250% of the rated voltage
Performance
Vibration Test
Capacitance change :
Tan
δ,
IR : initial spec.
Moisture
Resistance
Capacitance change :
Tan
δ
: 0.075 max
IR :
High Temperature
Resistance
500Mohm or 25Mohm
㎌
Whichever is Smaller
within ±12.5%
With 200%
within ±12.5%
within ±5%
Test condition
Amplitude : 1.5mm
From 10㎐ to 55㎐ (return : 1min.)
2hours
3 direction (x, y, z)
With rated voltage
40±2℃, 90~95%RH, 500+12/-0hrs
Capacitance change :
Tan
δ
: 0.075 max
IR :
of the rated voltage
Max. operating temperature
1000+48/-0hrs
1 cycle condition
Min. operating temperature
→
→
25℃
25℃
Max. operating temperature
→
1000Mohm or 50Mohm
㎌
Whichever is Smaller
within ±7.5%
Temperature
Cycling
Capacitance change :
Tan
δ,
IR : initial spec.
5 cycle test
C. Recommended Soldering method :
Reflow ( Reflow Peak Temperature : 260+0/-5℃, 10sec. Max )
* For the more detail Specification, Please refer to the Samsung MLCC catalogue.