MCH03
Ceramic capacitors
Multi-layer ceramic chip capacitors
MCH03
(0603 (0201) size, chip capacitor)
Features
1) Ultra miniature (0.6mm×0.3mm×0.3mm), Ultra light weight (0.3mg)
2) Suitable for mobile devices
3) Lead-free plating terminal
4) No polarity
Quick Reference
The design and specifications are subject to change without prior notice. Please check the most recent technical
specifications prior to placing orders or using the product. For more detail information regarding packaging style code,
please check product designation.
Thermal compensation
Part No.
Size code
Temperature characteristics
(ppm/°C)
code
Operating temp. range
(
°C
)
Rated voltage
(V)
Capacitance (pF)
Capacitance
tolerance
Thickness
(mm)
0
±
250(CK)
0
±
120(CJ)
MCH03
0603
A (AN)
0
±
60(CH)
−55
to
+125
25
0.5 to 2.7 (E12
Series)
∗
3.0 to 3.9 (E12
Series)
∗
4 to 5 (E12
Series)
∗
5.1 to 10 (E12
Series)
∗
11 to 100 (E12
Series)
C(±0.25pF)
D(±0.5pF)
J(
±
5%)
0.3
±
0.03
∗ :
0.5pF/0.75pF/2pF/3pF/4pF/5pF/6pF/7pF/8pF/9pF
available
High dielectric constant
Part No.
Size code
Temperature characteristics
code
Operating temp. range
(
°C
)
Rated voltage
(V)
Capacitance
(pF)
Capacitance
tolerance
Thickness
(mm)
±
10%(B)
CN
MCH03
0603
FN
−25
to
+85
−55
to
+125
−55
to
+85
−25
to
+85
−30
to
+85
±
15%
(R) (X7R)
±
15%(X5R)
+30%,
−80%
(F)
+22%,
−82%
(Y5V)
25
16
25
16
6.3
16
16
100 to 2,200 (E6 Series)
4,700 (E3 Series)
100 to 2,200 (E6 Series)
4,700 (E3 Series)
10,000 (E6 Series)
10,000 (E1 Series)
K (
±
10%)
0.3
±
0.03
Z (
+
80%,
−20%)
10,000 (E1 Series)
External dimensions
(Unit : mm)
0.6
±
0.03
0.3
±
0.03
0.3
±
0.03
0.1Min. 0.17Min.
0.3
±
0.03
0.3
±
0.03
Rev.A
1/12
MCH03
Ceramic capacitors
Product designation
Code Prduct thickness
K
0.3mm
Packing specification
Paper tape(width 8mm, pitch 2mm)
Reel
φ180mm
(7in.)
Basic ordering unit(pcs.)
15,000
Part No.
Packaging Style
M C H
Rated voltage
Code Voltage
8
3
2
6.3V
16V
25V
0 3
3
F N
1 0 3
Z
Nominal
capacitance
3-digit
designation
accordijg
to IEC
K
Capacitance tolerance
Tolerance
Code
C
D
J
K
Z
Temperature characteristic code
:Refer to quick reference table.
±
0.25pF(0.5 to 5pF)
±
0.5pF(5.1 to 10pF)
±
5%(11pF or more)
±
10%
+80%, −20%
Product No.list
•Thermal
compensation capacitors
Capacitance
(pF)
Temperature
A AN(CG) (COG) (CH) Characteristic
25V
Rated voltage (V)
Product No.
Tolerance Product thickness(mm)
MCH032A (AN) 0R5CK
MCH032A (AN) R75CK
MCH032A (AN) 010CK
MCH032A (AN) 1R2CK
MCH032A (AN) 1R5CK
MCH032A (AN) 1R8CK
MCH032A (AN) 020CK
MCH032A (AN) 2R2CK
C (
±
0.25pF)
MCH032A (AN) 2R7CK
MCH032A (AN) 030CK
MCH032A (AN) 3R3CK
MCH032A (AN) 3R9CK
0.6
±
0.03
MCH032A (AN) 040CK
MCH032A (AN) 4R7CK
MCH032A (AN) 050CK
MCH032A (AN) 5R6DK
MCH032A (AN) 060DK
MCH032A (AN) 6R8DK
MCH032A (AN) 070DK
D (
±
0.5pF)
MCH032A (AN) 080DK
MCH032A (AN) 8R2DK
MCH032A (AN) 090DK
MCH032A (AN) 100DK
Capacitance
(pF)
12
15
18
22
27
33
39
47
56
68
82
100
0.5
0.75
1.0
1.2
1.5
1.8
2.0
2.2
2.7
3.0
3.3
3.9
4.0
4.7
5.0
5.6
6
6.8
7
8
8.2
9
10
Temperature
A AN(CG) (COG) (CH) Characteristic
25V
Rated voltage (V)
Product No.
Tolerance Product thickness(mm)
MCH032A (AN) 120JK
MCH032A (AN) 150JK
MCH032A (AN) 180JK
MCH032A (AN) 220JK
MCH032A (AN) 270JK
MCH032A (AN) 330JK
J (
±
5%)
0.6
±
0.03
MCH032A (AN) 390JK
MCH032A (AN) 470JK
MCH032A (AN) 560JK
MCH032A (AN) 680JK
MCH032A (AN) 820JK
MCH032A (AN) 101JK
Rev.A
2/12
MCH03
Ceramic capacitors
•High
dielectric constant capacitors
Capacitance
(pF)
Temperature
Rated voltage (V)
Tolerance Product thickness(mm)
100
150
220
330
470
680
1,000
1,500
2,200
4,700
10,000
K (
±
10%)
0.6
±
0.03
CN (R) (B) (X7R) Characteristic
16V
25V
Product No.
Product No.
MCH032CN101KK
MCH032CN151KK
MCH032CN221KK
MCH032CN331KK
MCH032CN471KK
MCH032CN681KK
MCH032CN102KK
MCH032CN152KK
MCH032CN222KK
MCH033CN472KK
CN (X5R) Characteristic
6.3V
Product No.
MCH038CN103KK
Capacitance
(pF)
10,000
Temperature
FN(F) (Y5V) Characteristic
16V
Rated voltage (V)
Product No.
Tolerance Product thickness(mm)
MCH033FN103ZK
Z (
+
80%,
−
20%)
0.6
±
0.03
Rev.A
3/12
MCH03
Ceramic capacitors
•Performance
and test method
No.
1
Items
Appearance and
dimensions
Performance
Test Method
(As per JIS C 5101-1, JIS C 5101-10)
No marked defects shall be allowed As per 4.4 of JIS C 5101-1.
for appearance.
As per 4.5 of JIS C 5101-10
Dimensions shall be as specified the Using a Magnifier.
clause 4.
No dielectrical breakdown or other
damage shall be allowed.
2
Withstanding voltage
As per 4.6 of JIS C 5101-1.
As per 4.6.4 of JIS C 5101-10
Voltage shall be applied as per Table1.
Table 1
Charac-
Voltage
teristic
A, AN
300% Rated voltage
CN
250% Rated voltage
FN
Voltage shall be applied for 1 to 5s with
50mA charging and discharging curent.
3
Insulation resistance
Not less than 10000MΩ or
500MΩ
µF,
whichever is less.
(For products with rated voltage less
than 16V, it is not less than 10000MΩ
or 100MΩ
µF,
whichever is less.)
As per 4.5 of JIS C 5101-1.
As per 4.6.3 of JIS C 5101-10
Measurements shall be made after
60+/−5s period of the rated voltage
applied.
As per 4.7 of JIS C 5101-1.
As per 4.6.1 of JIS C 5101-10
Measurements shall be made under the
conditions specified in Table 2.
Table 2
Charac-
Frequency Voltage
teristic
< 1000 pF
> 1000 pF
−
1+/−0.1MHz
1+/−0.1kHz
A, AN
1+/−0.1Vrms. 1+/−0.1Vrms.
CN
1+/−0.1kHz
1+/−0.1Vrms.
FN
4
Capacitance
Capacitance shall be
within specified tolerance range.
5 Dielectric loss tangent
A, AN
Capacitance
<
30pF
tan
δ
< 100/(400+20C)%
−
<
Capacitance
−
30pF
tan
δ
< 0.1%
−
Rated voltage=25V
tan
δ
< 3.0%
−
Rated voltage=16V
tan
δ
< 5.0%
−
Rated voltage=6.3V
tan
δ
< 10.0%
−
Rated voltage=16V
tan
δ
< 10.0%
−
As per 4.8 of
JIS C 5101-1.
As per 4.6.2 of
JIS C 5101-10
Measurements shall be made under the
conditions specified in Table 2.
CN
FN
Rev.A
4/12
MCH03
Ceramic capacitors
No.
Items
Performance
Test Method
(As per JIS C 5101-1, JIS C 5101-10)
As per 4.24 of JIS C 5101-1.
As per 4.7 of JIS C 5101-10
Temperature coefficient shall be calculated
at 20°C and 85°C.
6 Temperature
characteristic
A, AN
Capacitance C < 2pF
−
0+/−250ppm/
°C
Capacitance C=3pF
0+/−120ppm/
°C
Capacitance C < 4pF
−
0+/−60ppm/
°C
(−55°C to
+125°C)
X7R
R
B
X5R
+/−15%
(−55°C to
+125°C)
+/−10%
(−25°C to
+85°C)
+/−15%
(−55°C to
+85°C)
CN
As per 4.24 of JIS C 5101-1.
As per 4.7 of JIS C 5101-10
If required, measurements shall be made
at a given temperature.
FN
+30%, −80%
(−25°C to
+85°C)
+22%, −82%
(−30°C to
+85°C)
7 Solderability
More than 3/4 of each end
termination shall be covered with
new solder.
As per 4.15.2 of JIS C 5101-1.
As per 4.11 of JIS C 5101-10
The solder specified in JIS Z 3282 H63A
shall be used. Ans the flux containing 25%
rosin and ethanol solution shall be used.
The specimens shall be immersed into the
solder at 235+/−5°C
for 2+/−0.5s
So that both end terminations are
completely under solder.
As per 4.14 of
JIS C 5101-1.
As per 4.10 of
JIS C 5101-10
The solder specified in JIS Z 3282. H63A
shall be used.
The specimens shall be immersed into the
solder at 260+/−5
°C
for
5+/−0.5s so that
both end terminations are completely
under the solder.
Pre-heating at 150+/−10
°C
for 1 to 2min
Initial measurements prior to test shall be
performed after the thermal
Pre-conditioning specified in Remarks (1).
Final measurements shall be made after the
specimens have been left at room
temperature as per Table3.
Table3
Charac-
teristic
A, AN
CN, FN
Time
24+/−2 h
48+/−4 h
8 Resistance
to solderin
heat
Appearance Without mechanical damage.
Change
rate from
initial value
A, AN
Within
+/−2.5%
or
+/−0.25pF
whichever
is larger.
Within
+/−7.5%
Within
+/−20%
CN
FN
Dielectric
loss
tangent
Insulation
resistance
Within specified initial value.
Within specified initial value.
Withstanding No defects shall be allowed.
voltage
9 End termination
adherence
Without peeling or sign of
peeling shall be allowed
on the end terminations.
As per 4.13 of JIS C 5101-1.
As per 4.8 ofJIS C 5101-10
A 2N weight for
10+/−1s shall be applied
to the soldered specimens as shown by the
arrow mark in the below sketch.
Applied pressure
Substrate
Capacitor
Rev.A
5/12