MOLDED PARTS
Qualtek Electronics
QMB
HEAT SHRINKABLE MEDIUM VOLTAGE BREAKOUT
UP TO 36kV
Features/Applications
Medium voltage breakouts are made from radiation cross-linked
polyolefin. This specially designed material performs exceptionally
as an electrical insulator. The material will not crack and is UV
resistant, weather proof and flame retardant. These breakouts can
be safely used in protecting cable ends up to 36kV from flashover
or surges created while working with switchgear and transformer
boxes.
Operating temperature: -55°C
to +105°C
Minimum shrink temperature: 110°C
Full Recovery Temperature: 120°C
Standard color: Red
RoHS Compliant
Technical Data
Property
Operating Temperature
Tensile Strength
Tensile Strength After Thermal Aging (120°C,
168 hrs.)
Elongation at Break
Elongation at Break After Thermal Aging (120°C, 168 hrs.)
Water Absorption
Volume Resistance
Dielectric Strength
Tracking Resistance
Test Method
IEC 216
ASTM D 2671
ASTM D 2671
ASTM D 2671
ASTM D 2671
ISO 62
IEC 93
IEC 243
ASTM D 2303
Typical Data
-55°C
to +105°C
8 MPa min.
7 MPa min.
300% min.
200% min.
1% max.
10
13
Ω
.cm (min.)
20 kV / mm (min.)
Non-tracking
Product Dimensions
Part
Number
QMB 320-60/24
QMB 330-80/38
QMB 340-110/50
QMB 350-125/57
QMB 360-140/70
QMB 370-170/77
Notes:
(a) as supplied
(b) after recovery
D (mm)
a (Min.)
60
80
110
125
140
170
b (Max.)
24
38
50
57
70
77
l (mm)
a (Min.)
25
35
46
55
62
75
b (Max.)
8
11
17.5
20
26
28
Recovered Length
± 10%
L (mm)
180
210
250
260
280
280
F (mm)
45
57
65
57
70
80
Recovered Wall
± 10%
Dw (mm)
3.0
4.0
4.0
4.0
4.0
4.0
lw (mm)
2.5
4.0
4.0
4.0
4.0
4.0
ISO-9001 Company
www.qualtekusa.com
QMB-200C